Uploader Comments (modernblacksmith)
Top Comments
-
I would like the knife because when im in my shop im always looking for something to cut something and never can find one and my cheapy scissors always get broken so i think that knife would be extremely useful. thanks for your consideration
-
@modernblacksmith I think CCSInventions should get it too :D Mostly because more then one person would have a use for it... since I work in his shop a lot...
Video Responses
All Comments (53)
-
Great fuckin video! ;)
-
Ha ha zombies! Love that blade. I'm probably too late but I WANT IT! Why? Because of the M.B. stamp that's why. Would love to finish it
-
i want it and i want it cuz i think im gonna be good cuz i like doing things like this cuz its so mush fun and its a good reword
-
thats a big knife out of a smal fiell
-
@shortfusedleathernk The tang that was on the file before had broken off.
-
Why not leave the tang that was already there on the file instead of doing another?? If you said why I missed it , thanks , Kirby
-
"Yeah I'm wearing my gloves, wearing my glasses, Stop giving me hard times"
Hahahah you're the man LOL
Nevermind if the contest is over
I definitly subscribed : )
-
i would like it because i would like it.. it be a bush craft knife
haha just curious were you drunk?
Infantrymyers 4 months ago
@Infantrymyers hardly a day goes by when I'm not!
modernblacksmith 4 months ago 3
Is file steel similar to railroad spike steel?
hoshnasi 7 months ago
@hoshnasi more carbon in a file not all railroad spikes are the same it varies as much as rebar does
modernblacksmith 7 months ago
Really cool knife Dan, Did the file you used around 12:50 get ruined since it was (I'm guessing) the same grade of high carbon steel as the knife?
samdurnford 7 months ago
@samdurnford nope, as the steel had been heated and not quenched it was a level lower in hardness would be better to use a finer file on harder materials though.
modernblacksmith 7 months ago